[lammps-users] tensile of binary system

If you have a free surface and you do a minimization or run dyanmics,
the atoms are free to go where they want to go. The resulting
stress is the value it wants to be at equilibrium. What are you
imagining is the
physical mechanism acting on a free surface that drives the stress
to be some other value?