I am trying to study the radiation damage of graphite and there must be a lot of specific dislocation loops to be form. Ca you please guide me if there is a way to do that?
Thanks
I am trying to study the radiation damage of graphite and there must be a lot of specific dislocation loops to be form. Ca you please guide me if there is a way to do that?
Thanks
You can try OVITO’s Dislocation Analysis Modifier. Currently, simple crystal structures such as FCC, HCP, BCC, and diamond are supported. Please have a look at the linked manual entry for more details.